Polymer with molecular chain bearing
highly reactive functional groups, imparting high mechanical
strength without impairing flowability. Low-quantity
functional group content, enabling high-level balance
of engineering plastics modification and compatibilization.
Modification also enhances adhesion to metals and other
resins. It is supplied in pellet form.
Modification of polyamides
(PA) and other engineering plastics, for high impact strength.
Compatibilization. Adhesives and sealants component.
Basic characteristics of Tuftec™
M1911
Property
Test method
Value
Specific gravity
ASTM D 297
0.91
MFR (g/10 min)
230°C, 2.16 kg load
ASTM D 1238
4.5
Hardness
Type A
JIS K 6253
84
Tensile strength (MPa)
#3 dumbbell, 500 mm/min
JIS K 6251
21.6
Elongation (%)
#3 dumbbell, 500 mm/min
650
300% tensile stress
(MPa)
4.1
Styrene/(ethylene/butylene)
(wt%)
Asahi Kasei method
30/70
Acid value
(mg CH3ONa/g polymer)
Asahi Kasei method
(titration)
2
Product
form
–
Pellet
Please note that all data
and values are given as typical results obtained with the
indicated test methods for purposes of basic reference in
grade selection only, and not as any product specification
or warranty of any nature, and are subject to change without
notice.