Click on Grade No. for basic profile

Asaflex™ high-performance clear styrenic copolymer   Asaflex™ i-series Grade No. 805 810 815 825 830 835 840 845 i-100 i-350(Waxed) Typical Processing Injection molding Films, sheets Sheets Injection molding Blow molding Films, sheets Sheets Injection molding Films, sheets Sheets Shrink films Films, sheets Special characteristics Transparency Appearance Stiffness Surface hardness Styrenics impact strength Hinge Styrenics compatibility Bi-axially balanced extruded sheets Impact strength Transparency Thermal stability Property balance Transparency Impact strength Property balance Thermal stability GPPS compatible Impact strength Transparency Thermal stability Styrenics compatibility Thermal stability Property Method Units     (waxed)      (waxed)    (waxed)      Density ISO1183 kg/m3 1.02103 1.01103 1.02103 1.01103 1.02103 1.01103 1.02103 Water absorption ISO62 % <0.1 <0.1 <0.1 <0.1 <0.1 <0.1 <0.1 MFR (200°C, 5 kg load) ISO 1133 g/10 min 10 5 6 5 7 6 8 Mold shrinkage - % 0.2-0.8 0.2-0.8 0.2-0.8 0.2-0.8 0.2-0.8 0.2-0.8 0.2-0.8 Tensile strength 1 ISO 527-1 MPa 30 20 27 18 27 21 16 Elongation 1 % 15 250 200 250 40 220 170 Flexural strength ISO 178 MPa 50 24 37 21 34 24 24 Flexural modulus MPa 1,550 1,400 1,200 1,100 1,500 1200 1120 Rockwell hardness ISO 2039-2 - HRR 88 HRR<10 HRR 55 HRR<10 HRR<10 HRR<10 HRR<10 Durometer hardness ISO 868 - HDD 75 HDD 62 HDD 71 HDD 55 HDD 68 HDD 58 HDD 64 Charpy imp. strength 2, unnotched ISO 179 kJ/m2 16 NB 100 NB NB NB NB Charpy imp. strength2, V-notched kJ/m2 1.3 P 2 P 2 NB P Heat dist. temp. 3 ISO 75-1 °C 63 65 57 60 62 60 - Vicat softening point 4 ISO 306 °C 91 83 82 72 81 78 - Total light trans.5 ISO 3537 % 90 89 90 89 88 90 89 Haze 5 % 0.5 1.2 0.5 2 1.2 2 1.0 Typical applications Cosmetics caps Food containers Laminate films Food containers Hi-transparency blister packs Cosmetics caps Gardening ampoules Laminate films Shrink films Shrink films Transparent, hi-impact blister packs Laminate films Shrink films Drink cups Food containers Shrink films Food containers

¹ At 5 mm/min for Asaflex™ 805, and at 50 mm/min for all other grades.

2	Value at fracture into two or more pieces;	NB, non-break at 15 J;
		P, partial break at 15 J.

³ Non-annealed, 1.8 MPa load, 3 mm width.
⁴ 10 N load, 50 K/h
⁵ 2 mm plate.

Please note that all data and values are given as typical results obtained with the indicated test methods for purposes of
basic reference in grade selection only, and not as any product specification or warranty of any nature,
and are subject to change without notice.