| Home > Products
> Asaflex™ >Table
of Asaflex™ Grades and Properties >Asaflex™ 830 |
December
12, 2001
|
 |
|
Asaflex™
830
High-performance clear styrenic copolymer |
|
| Essentials |
Film and sheet extrusion grade. Blended
with SC*, for films with good balance of performance
characteristics. Capability for inflation and sheet
extrusion. It is supplied in pellet form.
Contact
us for information on handling and use.
| * |
Styrenic copolymer from PS Japan
Corp. similar to Asaflex™ 830 in refraction
index, resulting in blends that provide sheet transparency
significantly higher than attainable with any GPPS
(general-purpose polystyrene). |
|
|
| Basic characteristics of Asaflex™ 830 |
| Property |
Test method |
Value |
| Density (kg/m3) |
ISO 1183 |
1.01 103 |
| MFR, 200°C, 5 kg
load (g/10 min) |
ISO 1133 |
5 |
| Water absorption (%) |
ISO 062 |
<0.1 |
| Mold shrinkage (%) |
- |
0.2 - 0.8 |
| Tensile strength, 50
mm/min (MPa) |
ISO 527-1 |
18 |
| Elongation, 50 mm/min
(%) |
ISO 527-1 |
250 |
| Flexural strength (MPa) |
ISO 178 |
21 |
| Flexural modulus (MPa) |
ISO 178 |
1,100 |
| Rockwell
hardness |
ISO
2039-2 |
HRR
<10 |
| Durometer
hardness |
ISO
868 |
HDD
55 |
| Charpy
impact strength*, unnotched (kJ/m2) |
ISO
179 |
NB |
| Charpy
impact strength*, V-notched (kJ/m2) |
ISO
179 |
P |
Heat
distortion temp.,
non-annealed,, 1.8 MPa load, 120 K/h (°C) |
ISO
75-1 |
60 |
| Vicat
softening point, 10 N load, 50 K/h (°C) |
ISO
306 |
72 |
| Total
light transmission, 2 mm thick plate (%) |
ISO
3537 |
89 |
| Haze,
2 mm thick plate (%) |
ISO
3537 |
2 |
|
| *Value at fracture
into two or more pieces; |
NB, non-break at
15 J;
P, partial break at 15 J. |
| Please note that all data
and values are given as typical results obtained with the
indicated test methods for purposes of basic reference in
grade selection only, and not as any product specification
or warranty of any nature, and are subject to change without
notice. |
To top |
|