| Essentials |
|
Film and sheet grade. Styrenic resins
modifier, for high impact strength. Small-quantity addition
to GPPS (general-purpose polystyrene) for sheets with
good hinge characteristics and films with good elongation
characteristics. Inflation and sheet extrusion capability.
It is supplied in pellet form.
Contact
us for information on handling and use.
|
|
| Applications |
|
Blended with GPPS for PSP*
laminated, blister packs, and other films. Also as modifier
to heighten deep-drawing performance, for frozen dessert
cups and lids, and transparent cold-drink cups.
Laminate
film, Food containers, Frozen dessert cups
|
|
*PSP; Polystyrene paper (foamed PS)
| Basic characteristics of Asaflex™ 810 |
| Property |
Test method |
Value |
| Density (kg/m3) |
ISO 1183 |
1.01 103 |
| MFR, 200°C, 5 kg
load (g/10 min) |
ISO 1133 |
5 |
| Water absorption (%) |
ISO 062 |
< 0.1 |
| Mold shrinkage (%) |
- |
0.2 - 0.8 |
| Tensile strength, 50
mm/min (MPa) |
ISO 527-1 |
20 |
| Elongation, 50 mm/min
(%) |
ISO 527-1 |
250 |
| Flexural strength (MPa) |
ISO 178 |
24 |
| Flexural modulus (MPa) |
ISO 178 |
1,400 |
| Rockwell
hardness |
ISO
2039-2 |
HRR
< 10 |
| Durometer
hardness |
ISO
868 |
HDD
62 |
| Charpy
impact strength*, unnotched (kJ/m2) |
ISO
179 |
NB |
| Charpy
impact strength*, V-notched (kJ/m2) |
ISO
179 |
P |
Heat
distortion temp.,
non-annealed, 1.8 MPa load, 120 K/h (°C) |
ISO
75-1 |
65 |
| Vicat
softening point, 10 N load, 50 K/h (°C) |
ISO
306 |
83 |
| Total
light transmission, 2 mm thick plate (%) |
ISO
3537 |
89 |
| Haze,
2 mm thick plate (%) |
ISO
3537 |
1.2 |
|
| *Value at fracture
into two or more pieces; |
NB, non-break at 15 J;
P, partial break at 15 J. |
| Please note that all data
and values are given as typical results obtained with the
indicated test methods for purposes of basic reference in
grade selection only, and not as any product specification
or warranty of any nature, and are subject to change without
notice. |