| Essentials |
|
Injection molding grade. For molded
products with superior balance of high-level impact
strength and rigidity, maximum transparency, and good
surface appearance. It is supplied in pellet form.
Contact
us for information on handling and use.
|
|
| Applications |
| Food containers, cosmetics
caps, pencil cases and other stationery goods, toys, swim
goggle and other cases, consumer goods. |
|
| Basic characteristics of Asaflex™ 805 |
| Property |
Test method |
Value |
| Density (kg/m3) |
ISO 1183 |
1.02 103 |
| MFR, 200°C, 5 kg
load (g/10 min) |
ISO 1133 |
10 |
| Water absorption (%) |
ISO 062 |
<0.1 |
| Mold shrinkage (%) |
- |
0.2 - 0.8 |
| Tensile strength, 5
mm/min (MPa) |
ISO 527-1 |
30 |
| Elongation, 5 mm/min
(%) |
ISO 527-1 |
15 |
| Flexural strength (MPa) |
ISO 178 |
50 |
| Flexural modulus (MPa) |
ISO 178 |
1,550 |
| Rockwell
hardness |
ISO
2039-2 |
HRR
88 |
| Durometer
hardness |
ISO
868 |
HDD
75 |
| Charpy
impact strength*, unnotched (kJ/m2) |
ISO
179 |
16 |
| Charpy
impact strength*, V-notched (kJ/m2) |
ISO
179 |
1.3 |
Heat
distortion temp.,
non-annealed, 1.8 MPa load, 120 K/h (°C) |
ISO
75-1 |
63 |
| Vicat
softening point, 10 N load, 50 K/h (°C) |
ISO
306 |
91 |
| Total
light transmission, 2 mm thick plate (%) |
ISO
13468 |
90 |
| Haze,
2 mm thick plate (%) |
ISO
14782 |
0.5 |
|
| *Value at fracture into
two or more pieces. |
| Please note that all data
and values are given as typical results obtained with the
indicated test methods for purposes of basic reference in
grade selection only, and not as any product specification
or warranty of any nature, and are subject to change without
notice |
To top |